Filtek Z250 XT nano hybrid composite by 3M ESPE is a versatile nanohybrid restorative designed to deliver reliable strength and excellent aesthetics in everyday restorative procedures. Engineered with nano-sized particles, it provides wear resistance similar to microfills while outperforming other hybrids — with only 2.0% vol. polymerization shrinkage and compressive strength of 395 MPa.

Filtek Z250 XT Nano Hybrid Composite – Key Features

• Easy to Sculpt, Holds Its Shape — Maintains form prior to cure for precise anatomical contouring
• Does Not Stick to Instruments — Easy adaptation and shaping; streamlines clinical workflow
• No Slumping — Stays in place after placement without sagging
• Predictable Esthetics — Available in shades A1, A2, A3 matching Vita Classical Shade Guide
• High Strength — Compressive strength 395 MPa; flexural strength 155 MPa
• Low Polymerization Shrinkage — Only 2.0% vol.; reduces post-operative sensitivity
• Universal Application — Suitable for Class I–V restorations, core build-ups, and indirect restorations

Indications

• Direct anterior and posterior restorations (Class I–V)
• Core build-ups
• Splinting
• Indirect restorations — inlays, onlays, veneers

Key Specifications

• Type: Nano-hybrid light-cure resin composite
• Filler Content: 61% vol.
• Compressive Strength: 395 MPa
• Flexural Strength: 155 MPa
• Polymerization Shrinkage: 2.0% vol.
• Fracture Toughness: 1.5 MPa·m¹/²
• Composition: Silane treated silica, Bis-GMA, UDMA, TEGDMA, Aluminium oxide
• Available Shades: A1, A2, A3
• Brand: 3M ESPE
• Country of Origin: USA

Pack Contents

• 1 x Filtek Z250 XT Composite Syringe — 4g (select shade above)

Shipping Information

Dispatched within 1–2 working days. Worldwide delivery in 7–30 days via India Post. Import duties and customs charges are the buyer’s responsibility.

Returns Policy

100% money-back guarantee within 30 days of receipt. Contact us before returning goods.

Note: Images are for illustration purposes only. Packaging may vary. Latest available stock will be shipped.